31 |
- - Non Woven Geo Textiles |
Non Woven Geo Textiles |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Mass per unit area as per ASTM D 5261) |
1000.0 |
|
- (Tensile Strength as per ASTM D 4632) |
4000.0 |
|
- (Thickness as per IS 1060(P 5)Sec 3) |
1000.0 |
|
|
32 |
IS 164 : 2023 (2023) - Ready-Mixed Paint for Road Marking — Specification |
Ready-Mixed Paint for Road Marking — Specification |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
Table 1 (Drying time a) Surface dry (IS 101 (Part 3/sec 1))) |
600.0 |
|
Table 1 (Drying time b) Hard dry (IS 101 (Part 3/Sec 1))) |
600.0 |
|
Table 1 (Consistency) |
600.0 |
|
Table 1 (Finish, (IS 101 (Part 3/Sec 4))) |
600.0 |
|
Table 1 (Colour, (IS 101 (Part 4/Sec 2))) |
600.0 |
|
Table 1 (Wet opacity, percent, (IS 101 (Part 4/Sec 1))) |
600.0 |
|
Table 1 (Recoating property, Annexure E) |
600.0 |
|
Table 1 (Resistance to bleeding, Annexure F) |
600.0 |
|
Table 1 (Mass in kg/10 liter, (IS 101 (Part 1/Sec 7))) |
600.0 |
|
Table 1 (Keeping properties (12 Months), (IS 101 (Part 6/Sec 2))) |
5000.0 |
|
Table 1 (Early wash out resistance (for Type 2 only), Annexure G) |
1000.0 |
|
Table 1 (No pick up time (for type 2 only), Annexure H) |
1000.0 |
|
Table 1 (Non Volatile matter , (IS 101 (Part 8/sec 2))) |
600.0 |
|
Table 1 (Volume solid, (IS 101 (Part 8/sec 6))) |
800.0 |
|
Table 1 (Taber Abrasion resistance, mg weight loss after 500 cycles using CS10 wheel with 500 g on each load (for type 2 only), Annexure J) |
2000.0 |
|
Table 1 (Scrub resistance, Annexure K) |
2000.0 |
|
Table 1 (Resistance to accelerated weathering 500 hours (for type 2 only), Annexure L) |
30000.0 |
|
Table 1 (Flexibility (for type 2 only), (IS 101 (Part 5 /sec 2 ))) |
600.0 |
|
Table 1 (VOC, percent, (IS 101 (Part 2 /sec 4))) |
2000.0 |
|
Table 1 (Resistance to wear, Annexure M) |
3000.0 |
|
5.4 (Lead Restriction (IS 101 (Part 8/Sec 5), or by Atomic
Absorption Spectrometer (AAS) or by ICP.)) |
1000.0 |
|
|
33 |
- - Customs specification for Chemical NTH WR |
Customs specification for Chemical NTH WR |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Salt spray test for 100 hours) |
4000.0 |
|
|
34 |
IS 6956 : 2001(Reaffirmed 2022) - Cover paper-Specification |
Cover paper-Specification |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Burst Index (KPa.m²/g)) |
1000.0 |
|
- (pH) |
1000.0 |
|
- (Tensile Index(Nm/g)- MD) |
1000.0 |
|
- (Tensile Index(Nm/g)- CD) |
1000.0 |
|
- (Opacity Percent) |
1000.0 |
|
- (Brightness) |
2000.0 |
|
- (One minute Cobb Test (g/m²)) |
2000.0 |
|
- (Smoothness(Bendtsen)ml./min.) |
2000.0 |
|
- (Folding Endurance -MD) |
750.0 |
|
- (Folding Endurance -CD) |
750.0 |
|
- (Bending Stiffness Index,Nm⁶/Kg3 -MD) |
500.0 |
|
- (Bending Stiffness Index,Nm⁶/Kg3 -CD) |
500.0 |
|
- (Wax Pick) |
1000.0 |
|
- (Grammage (g/m²)) |
1000.0 |
|
|
35 |
IS 6956 (2001) - Cover paper - Specification (First Revision) |
Cover paper - Specification (First Revision) |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
No Record Found
|
|
36 |
IS 16415 (2015) - Composite cement |
Composite cement |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
No Record Found
|
|
37 |
IS 16415 (2015) - Composite cement - Specification |
Composite cement - Specification |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
Table 3,i (Fineness) |
1000.0 |
|
Table 3,iii,a (Setting Time-Initial) |
500.0 |
|
Table 3,iii,b (Setting Time-Final) |
500.0 |
|
Table-3 (Compressive strength - 24 h (±) 30 min) |
1000.0 |
|
Table-3,iv,a (Compressive strength-72(±)1 h) |
1000.0 |
|
Table-3,iv,b (Compressive strength-168(±)2 h) |
1000.0 |
|
Table-3,iv,c (Compressive strength-672(±)4 h) |
1000.0 |
|
|
38 |
1328 (1996) - Veneered Decorative Plywood |
Veneered Decorative Plywood |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
7 (Type (as per Cl 7.1.1 to 7.1.4 for Type 1 and 7.12.1 to 7.2.3 for Type 2)) |
1000.0 |
|
8.1 (Dimension, Length in mm) |
500.0 |
|
8.1 (Dimension, Width, in mm) |
500.0 |
|
8.1 (Thickness, in mm) |
500.0 |
|
8.3 (Edge Straightness, in mm / m) |
500.0 |
|
8.3 (Squareness, in mm / m) |
500.0 |
|
11.1.1 (Moisture content, in percent) |
1000.0 |
|
11.1.2.1 (Water Resistance Test for MR Grade,) |
1000.0 |
|
11.1.2.2 (Water Resistance Test for BWR Grade,) |
1000.0 |
|
|
39 |
Custom specification for General Chemical -NTH WR - - |
- |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Identification of material) |
2000.0 |
|
|
40 |
Custom specification for Fire & Flammability - Custom specification for Fire & Flammability- NTH WR chemical |
Custom specification for Fire & Flammability- NTH WR chemical |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Flammability) |
3000.0 |
|
- (Fire Resistance) |
3000.0 |
|
|
41 |
Customized Specification For Printed Paper - Customized Specification For Printed Paper |
Customized Specification For Printed Paper |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (GSM (Gram Per Square Meter)) |
1000.0 |
|
|
42 |
IS 4853 (1982) - Recommended practice for radiographic inspection of fusion welded butt joints in steel pipes (First Revision) |
Recommended practice for radiographic inspection of fusion welded butt joints in steel pipes (First Revision) |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
IS 4853 (Radiography) |
2000.0 |
|
|
43 |
Customized Specification For UPVC Fins 50mmx100mm. - Customized Specification For UPVC Fins 50mmx100mm. |
Customized Specification For UPVC Fins 50mmx100mm. |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Density on the lines of ASTM D 792) |
1000.0 |
|
- (Vicat Softening Point on the lines of ASTM D 1525) |
2000.0 |
|
- (Heat reversion test @100 Deg. 60 min. on the lines of EN 479:2018) |
2000.0 |
|
- (Tensile Strength as per ASTM D 638) |
2000.0 |
|
- (Flexural Modulus as per ASTM D 790) |
3000.0 |
|
- (Limiting Oxygen Index) |
5000.0 |
|
|
44 |
IS 12701:1996 - Rotational Moulded Polyethylene Water Storage Tanks |
Rotational Moulded Polyethylene Water Storage Tanks |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
As per table 1 (Minimum Bottom Thickness) |
1000.0 |
|
As per table 1 (Minimum Wall Thickness) |
1000.0 |
|
5.4 (Wall Thickness above effective height) |
1000.0 |
|
7.2 (Resistance to Impact) |
2000.0 |
|
7.4 (Tensile Strength) |
2000.0 |
|
7.5 (Flexural Modulus) |
2000.0 |
|
7.1 (Resistance to deformation) |
2000.0 |
|
|
45 |
AAR (1994) - Clean Silica Sand |
Clean Silica Sand |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
1.0 (Test for presence of impurities (Clay, looms, mica and other foreign matters)) |
500.0 |
|
2.1 (Solubility in HCl in 24 hours, %) |
1000.0 |
|
2.1.1 (Determination of Silica, %) |
2000.0 |
|
3.1 (Caking Test) |
1000.0 |
|
3.2 (Gradation Test, % passing) |
2000.0 |
|
|
46 |
Customized Specification For APP Modified Bituminous Sheet Membrane - Customized Specification For APP Modified Bituminous Sheet Membrane |
Customized Specification For APP Modified Bituminous Sheet Membrane |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Thickness as per EN 1849-1) |
1000.0 |
|
- (Tensile Strength in Transverse Direction as per EN 12311-1) |
2000.0 |
|
- (Elongation in Longitudinal Direction as per EN 12311-1) |
1000.0 |
|
- (Elongation in Transverse Direction as per EN 12311-1) |
1000.0 |
|
- (Tear Strength in Longitudinal direction as per ASTM D 5147) |
2000.0 |
|
- (Tear Strength in Transverse direction as per ASTM D 5147) |
2000.0 |
|
- (Softening Point as per ASTM D 36) |
2000.0 |
|
- (Flexibility at low temperature(-2deg. C) as per EN 1109) |
2000.0 |
|
- (Flow resistance @120 deg.C after 2 hours as per EN 1110) |
2000.0 |
|
- (Water absorption as per ASTM D 5147) |
2000.0 |
|
|
47 |
Customized Specification for General Purpose Silicon Sealant - Customized Specification for General Purpose Silicon Sealant |
Customized Specification for General Purpose Silicon Sealant |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Density at 25 Deg.C in gm./cc.) |
1000.0 |
|
- (Tensile Strength(Kg./cm2)) |
2000.0 |
|
- (Elongation at Break(%)) |
2000.0 |
|
- (Shore A Hardness) |
2000.0 |
|
- (Dielectric Strength) |
3000.0 |
|
|
48 |
IS 17545:2021 - WHITE CEMENT BASED POLYMERIC PUTTY |
WHITE CEMENT BASED POLYMERIC PUTTY |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
4.1 (Form and Condition) |
500.0 |
|
4.3 (Consistency) |
500.0 |
|
4.4 (Lead Restriction-ASTM D3335-85a.) |
1000.0 |
|
4.5 Table, 1, (i) (Average Tensile adhesion strength@ 14days-Annex B) |
2000.0 |
|
4.5, Table 1, (ii) (Water retentivity-Annex C) |
1000.0 |
|
4.5, Table 1, (iii) (Initial Setting time-Annex D) |
250.0 |
|
4.5, Table 1, (iii) (Final Setting time-Annex D) |
250.0 |
|
4.5, Table 1, (iv) (Polymer content(based on loss on ignition)-Annex E) |
1000.0 |
|
4.5, Table 1, (v) (Degree of whiteness-Annex B of IS 8042) |
2000.0 |
|
4.5, Table 1, (vi) (Cement content-Annex B of IS 5410) |
1000.0 |
|
4.6 Table 2 (28 days Compressive strength-IS 4031(6)) |
1000.0 |
|
custom (Potlife) |
1000.0 |
|
custom (Degree of whiteness) |
1500.0 |
|
custom (Fineness) |
1000.0 |
|
custom (Bulk density) |
1000.0 |
|
custom (Water absorption) |
1000.0 |
|
|
49 |
IS 17545: 2021 (2021) - WHITE CEMENT BASED POLYMERIC PUTTY |
WHITE CEMENT BASED POLYMERIC PUTTY |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
4.1 (FORM &CONDITION) |
100.0 |
|
4.3 (Consistency) |
100.0 |
|
4.4 (Lead Restriction ( as metallic lead)) |
1000.0 |
|
4.5 Table 1(i) (Tensile adhesion strength (avg. of min 3 readings)
@14 days, N/mm2,) |
2500.0 |
|
4.5 Table 1(ii) (Water retentivity, percent) |
1000.0 |
|
4.5 Table 1(iii) (Initial Setting time-Annex D in minutes) |
200.0 |
|
4.5 Table 1(iii) (Final Setting time-Annex D
in minutes) |
200.0 |
|
4.5 Table 1(iv) (Polymer content (based on loss on ignition), percent by mass) |
1000.0 |
|
4.5 Table 1(vi) (Cement content, percent
Annex B of IS 5410) |
1200.0 |
|
4.6 Optional requirement (Compressive strength, 28 days in N/mm2
(IS 4031 (Part 6))) |
3000.0 |
|
4.5 Table 1(v) (Degree of whiteness, percent) |
1200.0 |
|
|
50 |
Customized Specification for Waste Container(Dust Bin)(Dust Bin) - Customized Specification for Waste Container(Dust Bin) |
Customized Specification for Waste Container(Dust Bin) |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Material Identification) |
2000.0 |
|
- (Tensile Strength at Break as per ASTM D 638) |
2000.0 |
|
- (Elongation at Break as per ASTM D 638) |
2000.0 |
|
- (Volume capacity(Ltrs)) |
1000.0 |
|
- (Density as per ASTM D 792) |
1000.0 |
|
- (Ball Drop test @ 1Kg. from 0.3 M height(3times at different locations)on the lines of IS 12701:1996) |
2000.0 |
|
|
51 |
None - Association of American Railboard ( Silica Sand) |
Association of American Railboard ( Silica Sand) |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Solubility) |
1000.0 |
|
- (Silica content) |
1500.0 |
|
|
52 |
1865 (1991) - Iron Castings with Spheroidal or Nodular Graphite- Specification |
Iron Castings with Spheroidal or Nodular Graphite- Specification |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
12.1 (Tensile Strength as per IS 1608 Part 1 or relevant standard test method) |
1000.0 |
|
12.1 (0.2 percent proof stress ( Grade Specified in Table 1 of IS 1865) - Test method as per IS 1608 Part-1) |
1000.0 |
|
12.1 (Percentage of Elongation ( Grade Specified in Table 1 of IS 1865) - Test Method as per IS 1608 Pat-1) |
1000.0 |
|
12.2 (Impact Test carried out V-Notch Charpy Test as per IS 1757 ( Clause 12.2.1, 12.2.2. and 13.3.1 Table 3 and 4 of IS 1865)) |
5000.0 |
|
13.2 (Brinell Hardness Test as per IS 1500 Part-1 ( Specified in Annexure-A of IS 1865)) |
2000.0 |
|
A-5 (Microstructure as per IS 7754 ( Specification in Annexure A-5 of IS 1865)) |
3500.0 |
|
6 (Visual Examination as per IS 1865, Clause.61. and 6.2 with customer specified drawing) |
1000.0 |
|
8 (Visual Examination as per IS 1865 Cl.8.1 and 8.2) |
1000.0 |
|
0 (Dimension Measurement of Cast and Finished Product as per customer specified drawing with tolerances) |
1000.0 |
|
0 (Visual Examination of Finished Product as per customer specification) |
1000.0 |
|
|
53 |
None - Custom- Non Flammable Adhesive (Gen Chem) |
Custom- Non Flammable Adhesive (Gen Chem) |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Consistency) |
1000.0 |
|
- (Coverage) |
1000.0 |
|
- (Odour) |
500.0 |
|
- (Wet Strength) |
4500.0 |
|
- (Shear Strength) |
4500.0 |
|
- (Fire Resistance) |
3000.0 |
|
- (Drying Time) |
1000.0 |
|
- (Colour) |
500.0 |
|
|
54 |
BS 204 :2001 (2001) - Classification of Thermoplastic Wood Adhesives for Non-Structural Application |
Classification of Thermoplastic Wood Adhesives for Non-Structural Application |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
Table 2, Sl. No. 1 (Tensile Shear Strength of Lap Joints (Adhesion Strength) for Thin Bond Line, in N/sq mm.) |
4000.0 |
|
Table 2, Sl. No. 1 (Tensile Shear Strength of Lap Joints (Adhesion Strength) for Thick Bond Line, in N/sq mm.) |
4000.0 |
|
Table 2, Sl. No. 2 (Tensile Shear Strength of Lap Joints (Adhesion Strength) for Thin Bond Line, in N/sq mm. (After conditioning in water at 20 +/- 5 Deg for 3 hr followed by 7 days at Std Atmosphere)) |
5000.0 |
|
Table 2, Sl. No. 2 (Tensile Shear Strength of Lap Joints (Adhesion Strength) for Thick Bond Line, in N/sq mm. (After conditioning in water at 20 +/- 5 Deg for 3 hr followed by 7 days at Std Atmosphere)) |
5000.0 |
|
Table 2, Sl. No. 3 (Tensile Shear Strength of Lap Joints (Adhesion Strength) for Thin Bond Line, in N/sq mm. (After conditioning in water at 20 +/- 5 Deg for 4 days)) |
5000.0 |
|
Table 2, Sl. No. 3 (Tensile Shear Strength of Lap Joints (Adhesion Strength) for Thick Bond Line, in N/sq mm. (After conditioning in water at 20 +/- 5 Deg for 4 days)) |
5000.0 |
|
Table 2, Sl. No. 4 (Tensile Shear Strength of Lap Joints (Adhesion Strength) for Thin Bond Line, in N/sq mm. (After conditioning in water at 20 +/- 5 Deg for 4 days followed by 7 days in Std Atmosphere)) |
5000.0 |
|
Table 2, Sl. No. 4 (Tensile Shear Strength of Lap Joints (Adhesion Strength) for Thick Bond Line, in N/sq mm. (After conditioning in water at 20 +/- 5 Deg for 4 days followed by 7 days in Std Atmosphere)) |
5000.0 |
|
Table 2, Sl. No. 5 (Tensile Shear Strength of Lap Joints (Adhesion Strength) for Thin Bond Line, in N/sq mm. (After conditioning in boiling water for 3 hr followed by 2 hr in water at 20 +/- 5 Deg C).) |
6000.0 |
|
Table 2, Sl. No. 5 (Tensile Shear Strength of Lap Joints (Adhesion Strength) for Thick Bond Line, in N/sq mm. (After conditioning in boiling water for 3 hr followed by 2 hr in water at 20 +/- 5 Deg C).) |
6000.0 |
|
|
55 |
IS 2141 (2000) - Hot dip galvanized stay strand - Specification (Fourth Revision) |
Hot dip galvanized stay strand - Specification (Fourth Revision) |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
7 (Freedom from defect) |
1000.0 |
|
8.1 (Wrapping Test of wire) |
1000.0 |
|
9.1 (Breaking Force of Strand) |
3000.0 |
|
9.1 (Elongation of Strand) |
1000.0 |
|
8.1 (Wire Diameter) |
1000.0 |
|
9.2 (Mass of Zinc Coating) |
2000.0 |
|
4 (Sulphur) |
500.0 |
|
4 (Phosphorus) |
500.0 |
|
|
56 |
Customized Specification for APP Modified Polyester Reinforced Bitumen Membrane - APP Modified Polyester Reinforced Bitumen Membrane |
APP Modified Polyester Reinforced Bitumen Membrane |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Roll Size) |
500.0 |
|
- (Thickness as per ASTM D 5147) |
1000.0 |
|
- (Roll Weight) |
500.0 |
|
- (Softening Point as per ASTM D 36) |
1500.0 |
|
- (Tensile Strength in Longitudinal Direction as per ASTM D 5147, N/5cm) |
1000.0 |
|
- (Tensile Strength in Transverse Direction as per ASTM D 5147, N/5cm) |
1000.0 |
|
- (Elongation at break in Transverse Direction as per ASTM D 5147, %) |
1000.0 |
|
- (Elongation at break in Longitudinal Direction as per ASTM D 5147,%) |
1000.0 |
|
- (Tear Strength in Longitudinal Direction as per ASTM D 5147, N) |
2000.0 |
|
- (Tear Strength in Transverse Direction as per ASTM D 5147, N) |
2000.0 |
|
- (Water Absorption as per ASTM D 5147) |
2000.0 |
|
- (Compound Stability as per ASTM D 5147) |
2000.0 |
|
- (Low Temperature Flexibility as per ASTM D 5147) |
2000.0 |
|
- (Resistance to Ageing for 200hrs, UV as per ASTM G 154) |
12000.0 |
|
- (Ageing in Weather-O-Meter for 200hrs as per ASTM G 155) |
12000.0 |
|
- (Dimensional Stability in both directions as per ASTM D 5147) |
2000.0 |
|
- (Penetration in dm at 25 deg. as per ASTM D 5) |
1500.0 |
|
|
57 |
IS 277 (2018) - Galvanized Steel Sheets (Plain and Corrugated) |
Galvanized Steel Sheets (Plain and Corrugated) |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
14 ,15 (Dimensions) |
1000.0 |
|
3.3 (Thickness of sheet (uncoated), mm) |
1000.0 |
|
7 (Mass of Zinc coating ( Total Both sides)) |
2000.0 |
|
8.1 (Tensile Strength) |
2000.0 |
|
8.1 (Yield Stress) |
1000.0 |
|
8.1 (Elongation Percent) |
1000.0 |
|
8.2 (Bend Test) |
1000.0 |
|
12 (Freedom from Defects) |
1000.0 |
|
14 ,15 (Dimensions) |
1000.0 |
|
5.1 (Carbon, % by mass) |
500.0 |
|
5.1 (Manganese, % by mass) |
500.0 |
|
5.1 (Sulphur, % by mass) |
500.0 |
|
5.1 (Phosphorous, % by mass) |
500.0 |
|
0 (Coating Thickness of sheet at Top Side A, Bottom Side B and Total Coating Thickness) |
1500.0 |
|
0 (Uniformity of Zinc Coating) |
2000.0 |
|
5.1 (Chemical Compisitions in %, The base steel chemistry of galvanized sheets and
coils shall be as per Table 1. The Product analysis of
steel, when carried out either by the methods specified
in relevant parts of IS 228 or any other established
instrumental/chemical method) |
3500.0 |
|
3.3 (Thickness of Sheet ( Base Matel)) |
1000.0 |
|
|
58 |
Customized Specification for FLEXSEAL 4 mm. - Customized Specification for FLEXSEAL 4 mm. |
Customized Specification for FLEXSEAL 4 mm. |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Tensile Strength (Transverse) as per ASTM D 5147 (N/50mm.)) |
1000.0 |
|
- (Tensile Strength (Longitudinal) as per ASTM D 5147 (N/50mm.)) |
1000.0 |
|
- (Elongation as per ASTM D 5147 (Longitudinal)) |
1000.0 |
|
- (Elongation as per ASTM D 5147 (Transverse)) |
1000.0 |
|
- (Tear Strength(Longitudinal) as per ASTM D 5147) |
1000.0 |
|
- (Low Temperature Flexibility as per ASTM D 5147) |
3000.0 |
|
- (Compound Stability at 100 deg. C as per ASTM D 5147) |
3000.0 |
|
- (Dimensional Stability as per ASTM D 5147(Longitudinal)) |
1000.0 |
|
- (Dimensional Stability as per ASTM D 5147(Transverse)) |
1000.0 |
|
- (Tear Strength(Transverse) as per ASTM D 5147) |
1000.0 |
|
|
59 |
Customized Specification for Streseal - Customized Specification for Streseal |
Customized Specification for Streseal |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Tensile Strength as per ASTM D 4632(Longitudinal)) |
1000.0 |
|
- (Tensile Strength as per ASTM D 4632(Transverse)) |
1000.0 |
|
- (Elongation as per ASTM D 4632(Longitudinal)) |
1000.0 |
|
- (Elongation as per ASTM D 4632(Transverse)) |
1000.0 |
|
- (Penetration as per ASTM D 5) |
2000.0 |
|
- (Softening Point as per ASTM D 36) |
2000.0 |
|
- (Surface Texture(visual)) |
1000.0 |
|
- (Water absorption as per ASTM D 5147) |
2000.0 |
|
- (Top Surfacing(Visual)) |
1000.0 |
|
- (Mass per Unit area(Polyester reinforcement) as per ASTM D 3776) |
2000.0 |
|
- (Puncture Resistance test as per ASTM D 5602) |
2000.0 |
|
|
60 |
SMCCustomized Specification For SPRING LOADED SERIVCE CONNECTION BOX - SMC SPRING LOADED SERIVCE CONNECTION BOX |
SMC SPRING LOADED SERIVCE CONNECTION BOX |
- View breakup
-
Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
- (Flammability as per UL-94/IS-11731) |
5000.0 |
|
- (Glow wire test at 960 deg.C as per IS 11000) |
2000.0 |
|
- (Ball Pressure Test as per IEC-335) |
2000.0 |
|
- (UV ageing test for 200 hours) |
12000.0 |
|
- (Water absorption as per IS 13411:1992 Method 1) |
2000.0 |
|
- (Material Identification) |
1996.0 |
|
- (Glass Contents by Mass(Min.) as per IS 13410:1992) |
2000.0 |
|
- (Izod Impact Strength(Notched) as per IS 13410:1992) |
2000.0 |
|
- (Flexural Strength as per IS 13410:1992) |
2000.0 |
|
- (Tracking Resistance CTI,Min. as per IS 13410:1992) |
1000.0 |
|
- (Tensile Strength as per IS 13410:1992) |
4000.0 |
|
- (Density Of Moulding as per IS 13410:1992) |
1000.0 |
|
- (Volume Resistivity as per IS 13410:1992) |
1500.0 |
|
- (Surface Resistivity as per IS 13410:1992) |
1500.0 |
|
- (Dielectric Strength at 90deg.C in Oil) |
2000.0 |
|
- (Oxygen Index as per IS 13410:1992) |
4000.0 |
|
|