| 1 |
MMDTS 19041 Rev.03 - Technical Specification for Bio Degradable , Oleophobic & Hydrophobic Organic Surface Coating on Interior Surface |
Technical Specification for Bio Degradable , Oleophobic & Hydrophobic Organic Surface Coating on Interior Surface |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Drying time at 25±2°C (i) Surface dry, (ii) Curing time) |
2400.0 |
|
| 2 (Consistency) |
1200.0 |
|
| 3 (Finish) |
1200.0 |
|
| 4 (Colour) |
1200.0 |
|
| 5 (Dry film thickness per coat) |
1200.0 |
|
| 6 (Scratch hardness (at 1.5 Kg. load)) |
1200.0 |
|
| 7 (Flexibility & Adhesion (6.25 mm mandrel)) |
1200.0 |
|
| 8 (Flash Point) |
1200.0 |
|
| 9 (Resistance to Salt Spray (3000hrs)) |
150000.0 |
|
| 10 (Protection against corrosion under condensation (2500 hrs)) |
45000.0 |
|
| 11 (Spreading & Covering surface area Capacity) |
1200.0 |
|
| 12 (Resistance to chemicals On, 25% caustic soda solution (w/v)) |
1500.0 |
|
| 13 (Resistance to chemicals On, 30% Sulphuric Acid (v/v)) |
1500.0 |
|
| 14 (Mass in kg/10 litres,) |
1200.0 |
|
| 15 (Impact Resistance test) |
1500.0 |
|
| 16 (Resistance to distilled Water (3000hrs)) |
5000.0 |
|
| 17 (Abrasion Resistance test) |
5000.0 |
|
| 18 (Gloss at 60° angle of incidence) |
1200.0 |
|
| 19 (Anti-Graffiti Properties) |
5000.0 |
|
| 20 (Durability – Accelerated Weathering QUV 4 hours and 4hours Condensation alternatively, (750 hrs). Temp. 50°С as per ASTM G154- (latest version)) |
37500.0 |
|
|
| 2 |
EIL Specification for High Build Coating System - EIL Specification for High Build Coating System |
EIL Specification for High Build Coating System |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Cyclic Test Salt Spray : 72 hrs.
Drying in air: 16 hrs. UV-A340 nm weather meter: 80 hrs. One cycle: 168 hrs. (25 cycles at 168 hrs. each cycle) (ASTM D5894)) |
142000.0 |
|
| 2 (100% Humidity Test (ASTM D2247)) |
33000.0 |
|
| 3 (Thermal Shock Resistance Test:
5 cycles @ 30 minutes in furnace at 120 deg C and 15 minutes in water after quenching in water for each cycle.(ASTM D2485 method A)) |
5000.0 |
|
| 4 (Chemical resistance Test
ASTM D 543 10 % NaOH &40 % NaOH for 1000 hrs.) |
4000.0 |
|
| 5 (Chemical resistance Test ASTM D 543,5 %f H2SO4 for 168 hrs.) |
1500.0 |
|
| 6 (Chemical resistance Test ASTM D 543,Acetone for 4 weeks,) |
1500.0 |
|
| 7 (Chemical resistance Test , ASTM D 543 Xylene for 4 weeks) |
1500.0 |
|
| 8 (Chemical resistance Test, ASTM D 543 Ethanol for 4 weeks) |
1500.0 |
|
| 9 (Chemical resistance Test ASTM D 543,Kerosene for 4 weeks) |
1500.0 |
|
| 10 (Chemical resistance Test, ASTM D 543 Sea Water 2000 hrs.) |
4000.0 |
|
| 11 (Immersion in DM/DI water @90deg.C (ASTM C868) for 30 days) |
5000.0 |
|
| 12 (Cathodic Disbondment Test at 60 deg.C (ASTM G8)) |
5000.0 |
|
| 13 (Resistance to DM water using water immersion for 2000 hrs. ASTM D 870) |
2000.0 |
|
| 14 (Assessment of adhesion & Artificial Ageing as per ISO 19277) |
45600.0 |
|
|
| 3 |
M&C/PCN/132/2021 - RDSO Specification for Painting of Helical Coils Springs of LHB Coaches and similar application (single pack) |
RDSO Specification for Painting of Helical Coils Springs of LHB Coaches and similar application (single pack) |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Drying Time (Hard Dry)) |
1200.0 |
|
| 2 (Consistency) |
1200.0 |
|
| 3 (Finish) |
1200.0 |
|
| 4 (Colour) |
1200.0 |
|
| 5 ((a) Dry Film thickness,(b) Cumulative DFT) |
2400.0 |
|
| 6 (Volume solids %) |
2000.0 |
|
| 7 (Scratch Hardness (at 1.5 kg load)) |
1200.0 |
|
| 8 (Flexibility and Adhesion ( 6.25 mm Mandrel)) |
1200.0 |
|
| 9 (Flash Point) |
1200.0 |
|
| 10 (Resistance to Salt Spray 2000hrs.) |
100000.0 |
|
| 11 (Protection against Corrosion under condition of condensation 2000hrs.) |
36000.0 |
|
| 12 (Keeping properties (after 12 months)) |
5000.0 |
|
| 13 (Covering Capacity per coat) |
1200.0 |
|
| 14.(a) (Resistance to chemical (25% NaOH, w/v)) |
1500.0 |
|
| 14.(b) (Resistance to chemical (30% H2SO4, v/v)) |
1500.0 |
|
| 14.(c) (Resistance to chemical (20% HCL, v/v)) |
1500.0 |
|
| 14.(d) (Resistance to chemical (Lubricating oil)) |
1500.0 |
|
| 14. e. (i) (Resistance to solvent (Acetone)) |
1500.0 |
|
| 14. e. (ii) (Resistance to solvent (Xylene)) |
1500.0 |
|
| 14.e.(iii) (Resistance to solvent (Ethanol)) |
1500.0 |
|
| 14.(f) (Resistance to Raw water/ Tape water) |
1200.0 |
|
| 15 (Mass in kg/10 litres.) |
1200.0 |
|
| 16 (Impact Resistance Test) |
1500.0 |
|
| 17 (Fineness of Grind) |
1200.0 |
|
| 18 (Adhesion Test (Cross cut )) |
1500.0 |
|
| 19 (Disel Resistance Test) |
1200.0 |
|
| 20 (Abrasion Resistance Test of System) |
5000.0 |
|
| 21 (Pull of Adhesion) |
5000.0 |
|
| 22 (Cathodic Disbondment Test) |
5000.0 |
|
| 23 (Viscosity by Ford Cup no.4) |
1200.0 |
|
| 24 (Accelerated Weathering Test (QUV 500hrs)) |
25000.0 |
|
|
| 4 |
MMDTS 18034 REV-02 - Developmental Technical specification for PU Based Wet-On-Wet applicable Exterior
Painting System for LHB Type Coaches. |
Developmental Technical specification for PU Based Wet-On-Wet applicable Exterior
Painting System for LHB Type Coaches. |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (ANTI-GRAFFITI TEST,ASTM D-6578) |
5000.0 |
|
| 2 (Dry Film thickness) |
1200.0 |
|
| 3 (Weathering resistance (QUV 1000 hrs)) |
50000.0 |
|
| 4 (Corrosion resistance (ASTM B117, 1000 hrs)) |
50000.0 |
|
| 5 (Humidity Resistance (ASTM D2247, 500hrs)) |
15000.0 |
|
| 6 (Chemical Resistance (i) 30% Sulphuric acid, (ii) 20% NaOH) |
3000.0 |
|
| 7 (Abrasion resistance) |
5000.0 |
|
| 8 (Gloss ( after 72 hrs drying)) |
1200.0 |
|
| 9 (Natural weathering (upto one year)) |
5000.0 |
|
|
| 5 |
IS 2046-IS 2046 (1995) - Decorative thermosetting synthetic resinbonded laminated sheets specification (Second Revision) |
Decorative thermosetting synthetic resinbonded laminated sheets specification (Second Revision) |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 5.5 Table 7 Sl No Xi (Resistance to colour change in Xenon Arc light) |
5000.0 |
|
| 1 () |
- |
|
|
| 6 |
EIL B269_000_02_042_PCS_0001 Rev_3 - EIL system no. 7_Coating system - F7+F7+F7 = DFT 375 microns |
EIL system no. 7_Coating system - F7+F7+F7 = DFT 375 microns |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
No Record Found
|
|
| 7 |
IS 9968 : Part 1 (1984) - Elastomer Insulated Cables |
Elastomer Insulated Cables |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
No Record Found
|
|
| 8 |
IS 17048 (2018) - Halogen Free Flame Retardant (HFFR) Cables for Working Voltages up to and including 1100 Volts-Specification |
Halogen Free Flame Retardant (HFFR) Cables for Working Voltages up to and including 1100 Volts-Specification |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 15.6 Table 2 (iii) (a) (i) (Conductor Resistance Test) |
1500.0 |
|
| 15.6 Table 2 (iii) (a) (ii) (Annealing Test (For copper)) |
1000.0 |
|
| 15.6 Table 2 (iii) (b) (Test for Overall Dimensions and Thickness of Insulation and Sheath) |
1000.0 |
|
| 15.6 Table 2 (iii) (c) (iii) (Insulation Resistance Test) |
2000.0 |
|
| 15.6 Table 2 (iii) (c) (ii) or (iii) (f) (i) (High Voltage Test) |
1500.0 |
|
| 15.6 Table 2 (ii) (f) (Tensile strength and elongation at break) |
1500.0 |
|
| 15.6 Table 2 (iii) (c) (xiii) & (iii) (f) (v) (Flame Retardant Test) |
3000.0 |
|
| 15.6 Table 2 (iii) (f) (ii) (Flammability test) |
500.0 |
|
| - (Test on 2nd Core) |
2000.0 |
|
| - (Test on 3rd Core) |
2000.0 |
|
| - (Test on 4th Core) |
2000.0 |
|
|
| 9 |
AWWA C210 (2024) - Liquid - Epoxy Coatings and lining for Steel Water Pipe And fittings |
Liquid - Epoxy Coatings and lining for Steel Water Pipe And fittings |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| Additional Parameter (Colour) |
1000.0 |
|
| 5.5.2 (Appearance) |
1000.0 |
|
| 5.5.3 (Cure) |
1000.0 |
|
| 5.5.4 (Dry Film Thickness) |
1000.0 |
|
| 5.5.5 (Electrical Continuity) |
5000.0 |
|
| 5.5.6 (Pull of adhesion) |
5000.0 |
|
| 5.2.1 (Immersion & Vapor phase 30 days (DI Water)) |
2000.0 |
|
| 5.2.1 (Immersion & Vapor phase 30 days (Sulphuric acid 1% by wt.)) |
2000.0 |
|
| 5.2.1 (Immersion & Vapor phase 30 days (Sodium Hydroxide 1% by wt.)) |
2000.0 |
|
| 5.2.2 (Cathodic Disbondment Test) |
5000.0 |
|
| 5.2.3 (Dielectric Strength) |
2500.0 |
|
| 5.2.5 (Water Absorption) |
2000.0 |
|
| 5.2.6 (Water Vapor Transmission) |
5000.0 |
|
| Additional parameter (Drinking water test (as per annex 1 of IS 16676 : 2017)) |
12000.0 |
|
|
| 10 |
F-9 EIL SPEC B224-000-79-41-PLS-01 REV6 (2021) - F-9 Technical Name :Inoranic zinc silicate coating HRRL JOB SPECIFICATION FOR SURFACE PREPARATION AND PROTECTIVE COATINGS |
F-9 Technical Name :Inoranic zinc silicate coating HRRL JOB SPECIFICATION FOR SURFACE PREPARATION AND PROTECTIVE COATINGS |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
No Record Found
|
|
| 11 |
IS 15337 : 2003 (2003) - COAL TAR BASED ANTICORROSION TAPE FOR PROTECTION OF UNDERGROUND MILD STEEL PIPELINES - SPECIFICATION |
COAL TAR BASED ANTICORROSION TAPE FOR PROTECTION OF UNDERGROUND MILD STEEL PIPELINES - SPECIFICATION |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| Table No. 4 (Solubility of coal tar based tape in petrol (As per Annexure C of IS 15337)) |
1500.0 |
|
|
| 12 |
ILC PAINT SAMPLE (2023) - ILC PAINT SAMPLE |
ILC PAINT SAMPLE |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Drying Time , (a) Surface dry IS:101 Part 3 Section 1) |
400.0 |
|
| 2 (Drying Time , (b) Hard dry IS:101 Part 3 Section 1) |
400.0 |
|
| 3 (Drying Time , (c) Tack Free IS:101 Part 3 Section 1) |
400.0 |
|
| 4 (Colour as per IS:5) |
400.0 |
|
| 5 (Mass in Kg / Ten Litre as per IS:101 Part-1 Section-7) |
1200.0 |
|
| 6 (Scratch Hardness as per IS:101 Part-5 Section-2) |
1200.0 |
|
| 7 (Efflux Time (Consistency by flow cup B-4 Ford Cup) IS:101 Part-1 Section-5) |
1200.0 |
|
| 8 (Wet Opacity as per IS:101 Part-4 Section-1) |
1200.0 |
|
| 9 (Resistance to petrol Benzol Mixture as per IS:101 Part-7 Section-2 (Immersion method)) |
1200.0 |
|
| 11 (Gloss at 60
IS 101 (Part 4/Sec 4) : 2020) |
1000.0 |
|
| 12 (Flexibility and Adhesion
IS 101 part 5 sec 2 1988 RA 2019) |
1000.0 |
|
| 13 (Resistance to Humidity Under Conditions of Condensation
IS 101 part 6 sec 1 1988 RA 2020) |
1200.0 |
|
| 14 (Accelerated Storage Stability test
(IS 8982)) |
1200.0 |
|
| 15 (Resistance to Heat
IS 101 part 7 sec 3, 2020) |
1200.0 |
|
| 16 (Resistance to Warm Water
IS 8982) |
1200.0 |
|
| 17 (Resistance to Acid
IS 2932 2013) |
1200.0 |
|
| 18 (Resistance to Alkali
IS 2932:2013) |
1200.0 |
|
| 19 (Fineness of Grind in micron
IS 101 part 3 section 5 ,2019) |
1200.0 |
|
| 20 (Finish
IS 101 part 3 sec 4,1987 RA 2019) |
1200.0 |
|
| 21 (Volatile Matter
IS 101 part 2 sec 2 1986 RA 2017) |
1200.0 |
|
| 22 (Water Content
IS 101 part 2 sec 1 2018) |
1200.0 |
|
| 23 (Flash Point(Abel cup)
IS 101 part 1 sec 6 ,1987 RA 2019) |
1200.0 |
|
| 1 () |
- |
|
|
| 13 |
IS 109 (2017) - READY MIXED PAINT,
FINISHING, PRIMING, PLASTER, TO INDIAN
STANDARD COLOUR NO. 361 LIGHT STONE AND
NO. 631 LIGHT GREY, WHITE AND OFF-WHITE |
READY MIXED PAINT,
FINISHING, PRIMING, PLASTER, TO INDIAN
STANDARD COLOUR NO. 361 LIGHT STONE AND
NO. 631 LIGHT GREY, WHITE AND OFF-WHITE |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 4.1 (compostion) |
100.0 |
|
| 4.2 (Lead Restriction) |
- |
|
| 4.3 (i) a (Drying time Surface dry) |
1200.0 |
|
| 4.3 (i) b (Drying Time -Hard Dry) |
1200.0 |
|
| 4.3 (ii) (Finish) |
100.0 |
|
| 4.3 (iii) (Consistency) |
1200.0 |
|
| 4.3 (iv) (Mass, in kg/10 litre) |
100.0 |
|
| 4.3 (V) (Colour) |
100.0 |
|
| 4.3 (vi) (Wet opacity) |
100.0 |
|
| 4.3 vii (Flash point) |
400.0 |
|
| 4.3 (viii) (Water content) |
100.0 |
|
| 4.3 (ix) (Resistance to alkali) |
1500.0 |
|
| 4.3 (x) (Resistance to water) |
100.0 |
|
| 4.3 (xi) (Keeping properties) |
1500.0 |
|
| additional parameter 1 (Volatile Organic Compound) |
4000.0 |
|
| additional parameter 2 (Heavy Metal Content (Pb, Cr ,Cd ,Arsenic, Antimony &Mercury)) |
2500.0 |
|
|
| 14 |
JIS D5301:2006 and EN 50342-1:2006 - Customized Specification |
Customized Specification |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 9.5.2 (b) of JIS D5301:2006 (5 h rate Capacity test (C5) on 8 samples) |
50000.0 |
|
| 9.5.3 (b) of JIS D5301:2006 (High Rate Discharge Characteristics at (-)15 Deg C on 8 samples) |
80000.0 |
|
| 9.5.5 (b) of JIS D5301:2006 (Heavy Load Endurance Test at 40 ± 2 Deg C on 4 samples) |
180000.0 |
|
| 6.6 of EN 50342-1: 2006 (Endurance in Cycle Test at 40 ± 2 Deg C on 4 samples) |
100000.0 |
|
|
| 15 |
Berger Customer Specification -NTH ER Paint 1 (2022) - Berger Customer Specification -NTH ER Paint 1 |
Berger Customer Specification -NTH ER Paint 1 |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
No Record Found
|
|
| 16 |
AWWA C222-18 (2018) - Polyurethane Coatings and Linings for Steel Water Pipe and Fittings |
Polyurethane Coatings and Linings for Steel Water Pipe and Fittings |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| Prequalification requirements of polyurethane system (Resistance to UV Degradation ( ASTM G154)
4 h UV at 60 (±3) °C Black Panel Temperature;
4 h Condensation at 50 (±3) °C Black Panel Temperature) |
3500.0 |
|
| Prequalification requirements of polyurethane system (Appearance) |
1000.0 |
|
| Prequalification requirements of polyurethane system (Electrical continuity inspection(Holiday test)) |
3500.0 |
|
| Prequalification requirements of polyurethane system (Dry film thickness(DFT) microns) |
1000.0 |
|
| Prequalification requirements of polyurethane system (Adhesion to steel(pull off ) ASTM D4541) |
5000.0 |
|
| Prequalification requirements of polyurethane system (Hardness Shore D scale ASTM D2240) |
2000.0 |
|
| Prequalification requirements of polyurethane system (Water absorption ASTM D570) |
1500.0 |
|
| Prequalification requirements of polyurethane system (Dielectric strength. ASTM D149 (at 25 mils)) |
10000.0 |
|
| Prequalification requirements of polyurethane system (Chemical resistance 30 percent sodium hydroxide (NaOH), immersion test for 30 days
ASTM D543 Practice A) |
1500.0 |
|
| Prequalification requirements of polyurethane system (Chemical resistance 30 percent sodium chloride (NaCl), immersion test for 30 days
ASTM D543 Practice A) |
1500.0 |
|
| Prequalification requirements of polyurethane system (Chemical resistance 10 % sulfuric acid (H2SO4) immersion test for 30 days
ASTM D543 Practice A) |
1500.0 |
|
| Prequalification requirements of polyurethane system (Abrasion resistance CS17 wheel with a 1-kg weight (ASTM D4060 )) |
5000.0 |
|
| Prequalification requirements of polyurethane system (Impact resistance (ASTM G14)) |
2500.0 |
|
| Prequalification requirements of polyurethane system (Flexibility ASTM D522 Test Method B) |
1000.0 |
|
| 4 Polyurethane System Requirements (Cathodic disbondment (ASTM G8)) |
5000.0 |
|
| additional parameter (Adhesion to steel) |
1200.0 |
|
|
| 17 |
Corrosion Test (Salt Spray Test) as per ASTM B117 & Customer specification - Corrosion Test (Salt Spray Test) as per ASTM B117 & Customer specification |
Corrosion Test (Salt Spray Test) as per ASTM B117 & Customer specification |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| - (Corrosion Test (Salt Spray Test) for 48 Hrs. as per ASTM B117 & Customer specification) |
2500.0 |
|
| 2 (Drawing Identification) |
1500.0 |
|
|
| 18 |
F-6C EIL Specification No. 6-79-0020 Rev.1 (2024) - F-6C Solvent less epoxy Coating |
F-6C Solvent less epoxy Coating |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (Theoretical Covering capacity in sq.mt/coat/litre.) |
1500.0 |
|
| 4 (Weight per Litre) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.c) |
1200.0 |
|
| 7 (Full cure at 30 deg.C) |
1200.0 |
|
| 8 (Over-coat interval) |
1200.0 |
|
| 9 (Pot Life at 30 deg.C for Two Component Paints) |
1500.0 |
|
| 10 (Adhesion (ASTM D 4541)) |
5000.0 |
|
| 11 (Temperature Resistance (Min)) |
3000.0 |
|
|
| 19 |
F-6B EIL Specification No. 6-79-0020 Rev.1 (2024) - F-6B Epoxy High Build Coating |
F-6B Epoxy High Build Coating |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (Theoretical Covering capacity in sq.mt/coat/litre.) |
1500.0 |
|
| 4 (Weight per Litre) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.c) |
1200.0 |
|
| 7 (Full cure at 30 deg.C) |
1200.0 |
|
| 8 (Over-coat interval) |
1200.0 |
|
| 9 (Pot Life at 30 deg.C for Two Component Paints) |
1500.0 |
|
| 10 (Adhesion (ASTM D 4541)) |
5000.0 |
|
| 11 (Temperature Resistance (Min)) |
3000.0 |
|
|
| 20 |
F-6A EIL Specification No. 6-79-0020 Rev.1 (2024) - F-6A Epoxy High Build Coating |
F-6A Epoxy High Build Coating |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (Theoretical Covering capacity in sq.mt/coat/litre.) |
1500.0 |
|
| 4 (Weight per Litre) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.c) |
1200.0 |
|
| 7 (Full cure at 30 deg.C) |
1200.0 |
|
| 8 (Over-coat interval) |
1200.0 |
|
| 9 (Pot Life at 30 deg.C for Two Component Paints) |
1500.0 |
|
| 10 (Adhesion (ASTM D 4541)) |
5000.0 |
|
| 11 (Temperature Resistance (Min)) |
3000.0 |
|
|
| 21 |
F-17 EIL Specification No. 6-79-0020 Rev.1 (2024) - F-17 Novolac Epoxy Phenolic Coating Cured with Polyamine Adduct Hardener |
F-17 Novolac Epoxy Phenolic Coating Cured with Polyamine Adduct Hardener |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (Theoretical Covering capacity in sq.mt/coat/litre.) |
1500.0 |
|
| 4 (Weight per Litre) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.C) |
1200.0 |
|
| 7 (Full cure at 30 deg.C) |
1200.0 |
|
| 8 (Over-coat interval) |
1200.0 |
|
| 9 (Pot Life at 30 deg.C for Two Component Paints) |
1500.0 |
|
| 10 (Adhesion (ASTM D 4541)) |
5000.0 |
|
| 11 (Temperature Resistance (Min)) |
3000.0 |
|
|
| 22 |
F-15 EIL Specification No. 6-79-0020 Rev.1 - F-15, Two Component Epoxy Phenolic Coating Cured with Polyamine adduct Hardener |
F-15, Two Component Epoxy Phenolic Coating Cured with Polyamine adduct Hardener |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (Theoretical Covering capacity in sq.mt/coat/litre.) |
1500.0 |
|
| 4 (Weight per Litre) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.C) |
1200.0 |
|
| 7 (Full cure at 30 deg.C) |
1200.0 |
|
| 8 (Over-coat interval) |
1200.0 |
|
| 9 (Pot Life at 30 deg.C for Two Component Paints) |
1500.0 |
|
| 10 (Adhesion (ASTM D 4541)) |
5000.0 |
|
| 11 (Temperature Resistance (Min)) |
3000.0 |
|
|
| 23 |
F-12 EIL Specification No. 6-79-0020 Rev.1 (2024) - F-12 Heat Resistance Silicon Aluminium paint |
F-12 Heat Resistance Silicon Aluminium paint |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (Therotical Covering capacity in sq.mt/coat/litres) |
1500.0 |
|
| 4 (Weight per Litre) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.c) |
1200.0 |
|
| 7 (Over-coat interval) |
1200.0 |
|
| 8 (Temperature Resistance (Min)) |
3000.0 |
|
|
| 24 |
F14 EIL Specification No. 6-79-0020 Rev.1 (2014) - F-14 Polyamine cure coal tar epoxy |
F-14 Polyamine cure coal tar epoxy |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 4 (Weight per Litre) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.c) |
1200.0 |
|
| 7 (Full cure at 30 deg.) |
1200.0 |
|
| 8 (Over-coat interval) |
1200.0 |
|
| 9 (Pot Life at 30 deg.C for Two Component Paints) |
1500.0 |
|
| 10 (Adhesion (ASTM D 4541)) |
5000.0 |
|
| 11 (Temperature Resistance (Min)) |
3000.0 |
|
| 3 (Theoretical Covering capacity in sq.mt/coat/litre.) |
1500.0 |
|
|
| 25 |
F-11 EIL Specification No. 6-79-0020 Rev.1 - F-11 Heat Resistance synthetic medium based Two pack Aluminium paint |
F-11 Heat Resistance synthetic medium based Two pack Aluminium paint |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (.Therotical Covering capacity in sq.mt/coat/litres.) |
1500.0 |
|
| 4 (Weight per Litre) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.C) |
1200.0 |
|
| 7 (Over-coat interval) |
1200.0 |
|
| 8 (Temperature Resistance (Min)) |
1200.0 |
|
|
| 26 |
F-9 EIL Specification No. 6-79-0020 Rev.1 (2024) - F-9 Inorganic zinc silicate Coating |
F-9 Inorganic zinc silicate Coating |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (Theoretical Covering capacity in sq.mt/coat/litre) |
1500.0 |
|
| 4 (Weight per Litre) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg. C) |
1200.0 |
|
| 7 (Pot Life at 30 deg.C for Two Component Paints) |
1200.0 |
|
| 8 (Adhesion (ASTM D 4541)) |
5000.0 |
|
| 10 (Temperature Resistance (Min)) |
3000.0 |
|
| 9 (Over-coat interval) |
1200.0 |
|
|
| 27 |
F-7 EIL Specification No. 6-79-0020 Rev.1 (2024) - F-7 High build coal tar epoxy Coating |
F-7 High build coal tar epoxy Coating |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 3 (Therotical Covering capacity in sq.mt/coat/litres.) |
1500.0 |
|
| 4 (Weight per Litres) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.c) |
1200.0 |
|
| 7 (Full cure at 30 deg.C) |
1200.0 |
|
| 8 (Over-coat interval) |
1200.0 |
|
| 9 (Pot Life at 30 deg.C for Two Component Paints) |
1500.0 |
|
| 10 (Adhesion (ASTM D 4541)) |
5000.0 |
|
| 11 (Temperature Resistance (Min)) |
3000.0 |
|
|
| 28 |
P-4 EIL Specification No. 6-79-0020 Rev.1 (2024) - P-4 Etch Primer/Wash Primer |
P-4 Etch Primer/Wash Primer |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (Therotical Covering Capacity) |
1500.0 |
|
| 4 (Weight per Litres) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.c) |
1200.0 |
|
| 7 (Over-coat interval) |
1200.0 |
|
|
| 29 |
F-8 EIL Specification No. 6-79-0020 Rev.1 (2024) - F-8 Self priming type Surface tolerant High build coal tar epoxy Coating |
F-8 Self priming type Surface tolerant High build coal tar epoxy Coating |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (Theoretical Covering capacity in sq.mt/coat/litres) |
1500.0 |
|
| 4 (Weight per Litres) |
1200.0 |
|
| 5 (Touch dry at 30 deg.C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.c) |
1200.0 |
|
| 7 (Full cure at 30 deg.) |
1200.0 |
|
| 8 (Over-coat interval) |
1200.0 |
|
| 9 (Pot Life at 30 deg.C for Two Component Paints) |
1500.0 |
|
| 10 (Adhesion (ASTM D 4541)) |
5000.0 |
|
| 11 (Temperature Resistance (Min)) |
3000.0 |
|
|
| 30 |
F-2 EIL Specification No. 6-79-0020 Rev.1 (2024) - F-2 Acrylic Polyurethane Finish Paint |
F-2 Acrylic Polyurethane Finish Paint |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 1 (Volume Solid) |
2000.0 |
|
| 2 (Dry Film Thickness) |
1200.0 |
|
| 3 (Theoretical Covering capacity in sq.mt/coat/litres.) |
1500.0 |
|
| 4 (Weight per Litre) |
1200.0 |
|
| 5 (Touch dry at 30 deg. C) |
1200.0 |
|
| 6 (Hard Dry at 30 deg.c) |
1200.0 |
|
| 7 (Full cure at 30 deg.C) |
1200.0 |
|
| 8 (Over-coat interval) |
1200.0 |
|
| 9 (Pot Life at 30 deg.C for Two Component Paints) |
1500.0 |
|
| 10 (Adhesion (ASTM D 4541)) |
5000.0 |
|
| 11 (Abrasion Resistance (ASTM D4060)) |
5000.0 |
|
| 12 (Temperature Resistance (Min) deg. c (ASTM D 2485)) |
3000.0 |
|
|