| 151 |
IS 269 (2015) - Ordinary portland cement - Specification (Sixth Revision) |
Ordinary portland cement - Specification (Sixth Revision) |
- View breakup
-
| Clause No. |
Testing Charges (Excl. Of Taxes) |
NABL |
| 6.1, Table2, Sl No 8 (Alkali content IS 4032:1985) |
1000.0 |
|
| 6.1, Table2, Sl No 7 (Chloride content IS 4032:1985) |
500.0 |
|
| 6.1, Table2, Sl No 6 (Loss on ignition IS 4032:1985) |
600.0 |
|
| 6.1, Table2, Sl No 5 (Total Sulphur content percent by mass, IS 4032:1985) |
500.0 |
|
| 6.1, Table2, Sl No 4 (Magnesia IS 4032:1985) |
600.0 |
|
| 6.1, Table2, Sl No 3 (Insoluble residue, IS 4032:1985) |
600.0 |
|
| 6.1, Table2, Sl No 2 (Ratio of percentage of alumina to that of iron oxide IS 4032:1985) |
600.0 |
|
| 6.1, Table2, Sl No 1 (Ratio of percentage of lime to percentages of silica, alumina and iron oxide, IS 4032 : 1985) |
600.0 |
|
| 7, Table 3, Sl No 4c (Compressive strength, MPa (c) 672 ± 4 h IS 4031 (Part 6):1988) |
1000.0 |
|
| 7, Table 3, Sl No 4b (Compressive strength, MPa (b) 168 ± 2 h IS 4031 (Part 6):1988) |
1000.0 |
|
| 7, Table 3, Sl No 4a (Compressive strength, MPa-(a) 72 ± 1 h IS 4031 (Part 6):1988) |
1000.0 |
|
| 7, Table 3, Sl No 3b (Setting time: b) Final, IS 4031 (Part 5):1988) |
250.0 |
|
| 7, Table 3, Sl No 3a (Setting time: a) Initial IS 4031 (Part 5):1988) |
250.0 |
|
| 7, Table 3, Sl No 1 (Fineness IS 4031 (Part 2):1999) |
1000.0 |
|
| 7, Table 3, Sl No 2b (Soundness b) By autoclave test method IS 4031 (Part 3):1988) |
1000.0 |
|
| 7, Table 3, Sl No 2a (Soundness: a) By Le-Chatelier method, IS 4031 (Part 3):1988) |
500.0 |
|
| 6.1 Table 2 Note 2.a (Tricalcium aluminate content, percent by mass) |
- |
|
| 6.1 Table 2 Note 2.b (Tricalcium Silicate content, percent by mass, Minimum) |
- |
|
|